INSTALLATION INSTRUCTIONS
Masonry Anchor Strength Design Guide 2024
Installation Instructions For Use ( IFU ) are included with each product package . They can also be viewed or downloaded online at www . hilti . com . Because of the possibility of changes , always verify that downloaded IFU are current when used . Proper installation is critical to achieve full performance . Training is available on request . Contact Hilti Technical Services for applications and conditions not addressed in the IFU .
MATERIAL SPECIFICATIONS
Figure 3 — Hilti HIT-HY 200 A / R V3 adhesive cure time and working time ( approx .)
1 It is permitted to install Hilti HIT-HY 200 V3 with HIT-Z anchor rod down to 14 ° F ( -10 ° C ) provided the drilled hole has the drilling dust fully removed . This can be done with Hilti TE-CD or TE-YD hollow drill bit or with cleaning procedures used with standard threaded rod .
Resistance of cured Hilti HIT-HY 200 A / R V3 to chemicals
Chemical Behavior
Acetic acid |
10 % |
+ |
Acetone |
|
▯ |
Ammonia |
5 % |
+ |
Benzyl alcohol |
|
– |
Hydrochloric acid |
10 % |
▯ |
Chlorinated lime |
10 % |
+ |
Citric acid |
10 % |
+ |
Concrete plasticizer |
|
+ |
De-icing salt ( Calcium chloride ) |
|
+ |
Demineralized water |
|
+ |
Diesel fuel |
|
+ |
Drilling dust suspension pH 13.2 |
|
+ |
Ethanol |
96 % |
– |
Ethylacetate |
|
– |
Formic acid |
10 % |
+ |
Formwork oil |
|
+ |
Gasoline |
|
+ |
Glycole |
|
▯ |
Hydrogen peroxide |
10 % |
▯ |
Lactic acid |
10 % |
+ |
Maschinery oil |
|
+ |
Methylethylketon |
|
▯ |
Nitric acid |
10 % |
▯ |
Phosphoric acid |
10 % |
+ |
Potassium Hydroxide pH 13.2 |
|
+ |
Sea water |
|
+ |
Sewage sludge |
|
+ |
Sodium carbonate 10 % |
10 % |
+ |
Sodium hypochlorite 2 % |
2 % |
+ |
Sulphuric acid |
10 %
30 %
|
+
+
|
Toluene |
|
▯ |
Xylene |
|
▯ |
Key :
– non-resistant + resistant ▯ limited resistance
Samples of the HIT-HY 200 A / R V3 adhesive were immersed in the various chemical compounds for up to one year . At the end of the test period , the samples were analyzed . Any samples showing no visible damage and having less than a 25 % reduction in bending ( flexural ) strength were classified as “ Resistant .” Samples that had slight damage , such as small cracks , chips , etc . or reduction in bending strength of 25 % or more were classified as “ Limited Resistance ” ( i . e . exposed for 48 hours or less until chemical is cleaned up ). Samples that were heavily damaged or destroyed were classified as “ Non-Resistant .”
Note : In actual use , the majority of the adhesive is encased in the base material , leaving very little surface area exposed .
Masonry Fastening Technical Guide Edition 24 | 7.0 HIT-HY 200 V3 HYBRID FOR MASONRY CONSTRUCTION Hilti , Inc . 1-800-879-8000 | en español 1-800-879-5000 | www . hilti . com | Hilti ( Canada ) Corporation | www . hilti . ca | 1-800-363-4458