WU10PT |
HC-P15 |
An advanced PVD-TiAlN coating over a very deformation-resistant unalloyed carbide substrate. The WU10PT ™ grade’ s new and improved coating enables speeds to be increased by 50 – 100 %. The WU10PT grade is ideal for finishing to general machining of most workpiece materials at higher speeds. Excellent for machining most steels, stainless steels, cast irons, non-ferrous materials, and super alloys under stable conditions. It also performs well machining hardened and short chipping materials. |
M K N S H |
P |
|||
M |
|||
WU25PT |
An advanced PVD-TiAlN-coated grade with a tough, ultra-fine-grain, unalloyed substrate. For general-purpose machining of most steels, stainless steels, high-temperature alloys, titanium, irons, and non-ferrous materials. Speeds may vary from low to medium and will handle interruptions and high feed rates. |
K N S |
|
HC-P30 |
H |
Grade |
WU10HT |
A hard, low binder content, unalloyed WC / Co fine-grained uncoated grade. Exceptional edge wear resistance combined with very high strength for machining titanium, cast irons, austenitic stainless steels, non-ferrous metals, non-metals, and most high-temperature alloys. Superior thermal deformation and depth of cut notch resistance. The grain structure is well controlled for minimal pits and flaws, which contributes to long, reliable service. |
M K N S |
HW-K15 |
|||||
WP10CT |
HC-P10 |
A specially engineered, proprietary, cobalt-enriched carbide grade with thick K-MTCVD-TiCN coating layer, an Al 2 O 3 layer of controlled grain size, and outer layers of TiCN and TiN for maximum wear resistance. An excellent finishing to medium machining grade for a variety of workpiece materials including most steels, ferritic and martensitic stainless steels, and cast irons. The specially engineered cobalt-enriched substrate offers a balanced combination of deformation resistance and edge toughness, while the thick coating layers offer outstanding abrasion resistance and crater wear resistance for high-speed machining. The smooth coating provides good resistance to edge build-up and microchipping and produces excellent surface finishes. |
P
K
|
||
P |
|||||
|
WP25CT
widia. com
|
HC-P25 |
A tough cobalt-enriched carbide grade with a newly designed multilayer K-MTCVD TiCN- Al 2 O 3-TiCNTiN coating with superior interlayer adhesion. This is the industry’ s best general-purpose turning grade for most steels and ferritic and martensitic stainless steels. The substrate design, with cobalt-enrichment, ensures adequate deformation resistance along with excellent bulk toughness and insert edge strength. The coating layers offer good wear resistance over a wide range of machining conditions. The smoothness of the coating leads to reduced frictional heat, minimises microchipping, and improves workpiece surface finishes. |
K |
E11 |