PROFIS ENGINEERING REPORT TENSION LOAD
Bond Failure Mode
Equations N ba
( continued )
Equations ACI 318-14 Chapter 17 Provision Comments for PROFIS Engineering
N ba
= λ a т cr π da h ef
Example : Example of a table in an ICC-ESR showing characteristic bond stress values ( т kcr and т k , uncr ) and the seismic reduction value α N , seis .
Reference the Calculations section of the PROFIS Engineering report for more information on the parameter N ba
.
ICC-ESR-3187 Table 14
DESIGN INFORMATION Symbol Units
Nominal Rod Diameter ( in ). 3 / 8 1 / 2 5 / 8 3 / 4 7 / 8 1 1-1 / 4
Minimum Embedment h ef , min in 2-3 / 8 2-3 / 4 3-1 / 8 3-1 / 2 3-1 / 2 4 5 ( mm ) 60 70 79 89 89 102 127
Maximum Embedment h ef , max in 7-1 / 2 10 12-1 / 2 15 17-1 / 5 20 25 ( mm ) ( 191 ) ( 254 ) ( 318 ) ( 381 ) ( 445 ) ( 508 ) ( 635 )
Temperature Range A 2
Temperature Range B 2
Temperature Range C 2
Characteristic bond strength psi 1045 1135 1170 1260 1290 1325 1380 in cracked concrete т k , cr ( Mpa ) ( 7.2 ) ( 7.8 ) ( 8.1 ) ( 8.7 ) ( 8.9 ) ( 9.1 ) ( 9.5 )
Characteristic bond strength psi 2220 2220 2220 2220 2220 2220 2220 in uncracked concrete т k , uncr ( Mpa ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 )
Characteristic bond strength psi 1045 1135 1170 1260 1290 1325 1380 in cracked concrete т k , cr ( Mpa ) ( 7.20 ) ( 7.80 ) ( 8.00 ) ( 8.67 ) ( 9.00 ) ( 9.00 ) ( 9.50 )
Characteristic bond strength psi 2220 2220 2220 2220 2220 2220 2220 in uncracked concrete т k , uncr ( Mpa ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 ) ( 15.3 )
Characteristic bond strength psi 855 930 960 1035 1055 1085 1130 in cracked concrete т k , cr ( Mpa ) ( 5.9 ) ( 6.4 ) ( 6.6 ) ( 7.1 ) ( 7.3 ) ( 7.5 ) ( 7.8 )
Characteristic bond strength psi 1820 1820 1820 1820 1820 1820 1820 in uncracked concrete т k , uncr ( Mpa ) ( 12.6 ) ( 12.6 ) ( 12.6 ) ( 12.6 ) ( 12.6 ) ( 12.6 ) ( 12.6 )
Reduction for Seismic Tension α N , seis
- 0.88 1.0 1.0 1.0 1.0 0.97 1.0
1 Bond strength values correspond to concrete compressive strength f ́c = 2500 psi . For concrete compressive strength f ́c between 2500 psi and 800 psi , the tabulated characteristic bond strength may be increased by a factor of ( f ́c / 2500 ) 0 . 1 .
2 Temperature Range A : Maximum short term temperature = 130 ° F , Maximum long term temperature = 110 ° F . Temperature Range B : Maximum short term temperature = 176 ° F , Maximum long term temperature = 110 ° F . Temperature Range C : Maximum short term temperature = 248 ° F , Maximum long term temperature = 162 ° F . Short term elevated concrete temperatures are those which occur over brief intervals , e . g . as a result of diurnal cycling . Long term concrete temperatures are roughly constant over significant periods of time .
17 NORTH AMERICAN PROFIS ENGINEERING ANCHORING TO CONCRETE DESIGN GUIDE — ACI 318-14 Provisions